Brand Name : Anan
Model Number : PVC COMPOUND
Certification : UL,Reach,Rohs,ISO
Place of Origin : China
MOQ : 1000 kg
Price : 790-960USD/ton
Payment Terms : L/C, T/T
Supply Ability : 400 tons per month
Delivery Time : 5-7 days
Packaging Details : jumbo bag or little bag with 25kg
Color : Customised
Application : cable sheathing, Insulation
Material : Virgin Pvc Resin
Product name : Cable Pvc Compound
Usage : Electronic Wire,Plug,Cable
Appearance : smooth,Granule
Sample time : 5 working days
MOQ : 2000kgs
Density : 1.35-1.60g/cm3
Hardness : 75A~90A
About PVC Compounds:
Cable PVC compounds are thermoplastic materials derived from processing polyvinylchloride compositions, produced as granules. Various properties are imparted to compounds depending on applications and item operation conditions. This is achieved by using plasticizers, stabilizers and modifiers in various combinations in compositions.
PVC based plasticizers have considerable mechanical strength and water resistance, high thermal resistance to low temperatures, good insulation properties, insoluble in gasoline and kerosene, abrasion, acid and alkali resistant. PVC based compounds are readily welded and glued.
Cable PVC compounds are use in the cable and conductor industry for manufacture of insulation and protective wire and cable sheaths. The main final consumers of the PVC based cable and conductor products are energy and construction industries.
Here are two examples:
Softener formulation adjustment can raise the continuous operating temperature limit to 105°C.
Aluminium trihydroxide (ATH) additive can systematically reduce flammability and smoke formation. Regulatory authorities such as the VDE, EN or UL issue standardized property profiles for insulation and coating compounds.
Cable PVC Compounds Types:
Technical Data:
Items | Unit | Typical Value | Testing Method | ||
70 ℃ PVC Cable Compound | 105 ℃ PVC Cable Compound | 105 ℃ Irradiated crosslinked FR PVC Compound | |||
Tensile Strength | Mpa | 11 | 11 | 12 | GB/T 1040.3-2006 |
Elongation at Break | % | 180 | 180 | 180 | |
Heat Aging | |||||
Testing Termperature | ℃ | 100 | 135 | 135 | GB/T 8815-2008 |
Testing Time | h | 168 | 168 | 168 | |
Variation at tensile strength | % | 20 | 20 | 20 | |
Variation at elongation | % | -15 | -15 | -15 | |
Low Temperature Brittleness | ℃ | -20 | -20 | -20 | GB/T 5470-2008 |
Oxygen Index | / | ≥23 | ≥23 | ≥28 | GB/T 2406.2-2008 |
Density | g/cm3 | 1.42 | 1.42 | 1.42 | GB/T 1033.1-2008 |
Hardness | Shore A | 70-96 | 70-96 | 70-96 | GB/T 2411-2008 |
![]() |